Preparation of low-temperature sintered high conductivity inks based on nanosilver self-assembled on surface of graphene
LIU Piao(刘飘)1, HE Wen-qiang(贺文强)1, LU An-xian(卢安贤)2

1. Hunan LEED Electronic Ink Co., Ltd., Zhuzhou 412007, China;
2. School of Materials Science and Engineering, Central South University, Changsha 410083, China

Abstract:Finer nanoplates of silver are prepared by self-assembly on the surface of graphene, and the low-temperature sintered high conductivity ink containing the silver nanoplates is prepared. Most importantly, graphene is added to the solution before the chemical reduction reaction occurs. Firstly, it is found that silver nanoplates have self-assembly phenomenon on the surface of graphene. Secondly, the Ag nano hexagonal platelets (AgNHPs) with small particle sizes (10 nm), narrow distribution and good dispersion are prepared. Especially, smaller sizes (10 nm) and narrower particle size distribution of AgNHPs particles can be easily controlled by using this process. Finally, the conductivity of the ink is excellent. For example, when the printed patterns were sintering at 150 °C, the resistivity of the ink(GE: 0.15 g/L) reached the minimum value of 2.2×10-6 W·cm. And the resistivity value was 3.7×10-6 Ω·cm, when it was sintered at 100 °C for 30 min. The conductive ink prepared can be used for the field of printing electronics as ink-jet printing ink.

 

Key words: Ag nanoparticles; graphene; self-assembly; conductive ink; electrical properties

中南大学学报(自然科学版)
  ISSN 1672-7207
CN 43-1426/N
ZDXZAC
中南大学学报(英文版)
  ISSN 2095-2899
CN 43-1516/TB
JCSTFT
版权所有:《中南大学学报(自然科学版、英文版)》编辑部
地 址:湖南省长沙市中南大学 邮编: 410083
电 话: 0731-88879765(中) 88836963(英) 传真: 0731-88877727
电子邮箱:zngdxb@csu.edu.cn 湘ICP备09001153号