均匀化工艺对Al-4.46Mg合金腐蚀和疲劳性能的影响
王在玲1,邓运来1, 2,伍鹏飞2,孙琳3,戴青松2,叶凌英2

(1. 中南大学 轻合金研究院,湖南 长沙,410083;
2. 中南大学 材料科学与工程学院,湖南 长沙,410083;
3. 中车青岛四方机车车辆股份有限公司,山东 青岛,266111
)

摘 要: 研究480 ℃/20 h,430 ℃/2 h+490 ℃/12 h和500 ℃/16 h这3种均匀化工艺对Al-Mg合金腐蚀性能和疲劳性能的影响;通过晶间腐蚀(IGC)和慢应变速率拉伸(SSRT)腐蚀研究这3种工艺对Al-Mg合金O态板材的腐蚀性能的影响;通过疲劳裂纹扩展速率和Kahn撕裂实验研究这3种工艺对Al-Mg合金O态板材疲劳性能的影响。研究结果表明:与其他2种工艺相比,经430 ℃/2 h+490 ℃/12 h均匀化后得到的板材抗晶间腐蚀性能最佳,腐蚀速率为2.287 8 mg/cm2,应力腐蚀敏感指数ISSRT最小,为0.068;经430 ℃/2 h+490 ℃/12 h均匀化后得到的板材在高应力强度因子范围下抗裂纹扩展性能最佳,其单位面积裂纹形核功与经500 ℃/16 h处理得到的板材的形核功接近。

 

关键字: Al-Mg合金;均匀化;腐蚀性能;疲劳性能

Effect of homogenization on corrosion and fatigue performance of Al-4.46Mg alloy
WANG Zailing1, DENG Yunlai1, 2, WU Pengfei2, SUN Lin3, DAI Qingsong2, YE Lingying2

1. Light Alloy Research Institute, Central South University, Changsha 410083, China;
2 School of Materials Science and Engineering, Central South University, Changsha 410083, China;
3. CRRC Qingdao Sifang Co. Ltd, Qingdao 266111, China

Abstract:The effects of homogenization on corrosion and fatigue performance of Al-Mg alloy were studied after being homogenized using three homogenization technologies, i.e., 480 ℃/20 h, 430 ℃/2 h+490 ℃/12 h and 500 ℃/16 h, the corrosion performance of Al-Mg alloy sheets were tested by intergranular corrosion(IGC) and slow strain rate testing(SSRT), the fatigue performance of Al-Mg alloy sheets were tested by fatigue crack growth rate testing and Kahn tear test. The results show that Al-Mg alloy after homogenization by 430 ℃/2 h+490 ℃/12 h has the best intergranular corrosion resistance, the rate of corrosion is 2.287 8 mg/cm2, and the susceptibility index of slow strain rate test is 0.068. Al-Mg alloy after homogenization by 430 ℃/2 h+490 ℃/12 h has the best crack propagation resistance in the range of high intensity factor, and the unit initiation energy is close to that of the Al-Mg alloy sheets after annealing homogenization through the treatment at 500 ℃ for 16 h.

 

Key words: Al-Mg alloy; homogenization; corrosion performance; fatigues performance

中南大学学报(自然科学版)
  ISSN 1672-7207
CN 43-1426/N
ZDXZAC
中南大学学报(英文版)
  ISSN 2095-2899
CN 43-1516/TB
JCSTFT
版权所有:《中南大学学报(自然科学版、英文版)》编辑部
地 址:湖南省长沙市中南大学 邮编: 410083
电 话: 0731-88879765(中) 88836963(英) 传真: 0731-88877727
电子邮箱:zngdxb@csu.edu.cn 湘ICP备09001153号